PTFE lesela la mocheso o phahameng oa mocheso le boloka motlakase o babatsehang ho tloha ho -180°C ho ea ho 260°C: resistivity ea molumo >10¹³ Ω·cm ho 200°C, dielectric e tsitsitseng e tsitsitseng ho 2.0-2.1. Ka holimo ho 260°C, PTFE ea nolofatsa, e bola ka holimo ho 327°C, e lahleheloa ke ho intša ka ho sa feleng. Ka tlase ho 0 ° C, ho hloekisoa hoa ntlafala empa ho roala ho fetoha ho senyeha. Lula ka har'a 260 ° C bakeng sa ts'ebetso e tšepahalang.

Lesela la mocheso o phahameng oa PTFE (PTFE-coated fiberglass) le loketse bakeng sa mabanta a tsamaisang lijo ka lebaka la ho hanyetsa mocheso oa 260 ° C, -70 ° C ho fetoha ha maemo a batang, sebaka se sa thupeng, le ho lumellana le FDA. Lisebelisoa tsa bohlokoa: lionto tsa ho baka (libisikiti, bohobe, pitsa), lijana tsa lijo tse halikiloeng, lipompong tsa lipompong, lithanele tse hatsetsang, lintho tse koalang mocheso le ho phuthela lirolara. E fokotsa litšila le nako ea ho hloekisa.

Calendering - ho hatella lesela le koahetsoeng ke PTFE pakeng tsa lirolara tsa seipone tse futhumetseng ka 360-380 ° C - ho fetola ka mokhoa o makatsang sebopeho sa bokaholimo, thepa ea ho lokolla, ho se khonehe, le ts'ebetso ea mochini. E fokotsa boima ho tloha ho Ra 0.5-1.0 μm ho <0.05 μm, e tiisa li-pinholes, e ntlafatsa ho hanyetsa ho apara, empa e fokotsa matla a ho taboha le ho feto-fetoha ha maemo. E bohlokoa bakeng sa ho lokolla li-liner le ho kenya motlakase.

PTFE lesela la mocheso o phahameng oa mocheso le lesela la silicone ka bobeli li sebelisa lesela la fiberglass e le motheo empa li fapane ka thepa ea ho roala (PTFE resin vs silicone rabara). PTFE e ipabola tabeng ya ho se thure, ho se mamelle, le ho hanyetsa dikhemikhale ho fihla ho 260°C. Lesela la silicone le fana ka maemo a holimo, ho kenya motlakase, le ho hanyetsa mollo (ho fihlela ho 230 ° C). Khetha ho latela lintho tse tlang pele bophelong ba hau.

PTFE lesela la mocheso o phahameng oa mocheso (PTFE membrane material) ke khetho ea pele bakeng sa meralo e tsitsitseng. Melemo ea bohlokoa: lilemo tse 30+ tsa bophelo ba kantle, sebaka sa ho itlhoekisa (metsi a pula a hlatsoa litšila), phetiso ea mabone a bonolo (6-13%), boemo ba mollo oa Sehlopha sa A, le matla a kang tšepe a ka tlase ho 1.5 kg/m². E sebelisoa mabaleng a lipapali, boemafofaneng le meahong e ikhethang lefatšeng ka bophara.

PTFE impregnation ha e felle feela ho fiberglass lesela. Sengoliloeng sena se hlahisa li-substrates tse 7 tse ling - aramid, carbon fiber, PBI, porous metal, graphite, asbestos (fased out), le li-filler tsa ceramic - ka likarolo tsa bona tsa ts'ebetso, melemo, mefokolo, le lits'ebetso tsa bohlokoa.

Sengoliloeng sena se hlalosa hore na ke hobane'ng ha lesela la fiberglass e se nang alkali e le eona substrate e ratoang bakeng sa lesela la mocheso o phahameng oa PTFE. E akaretsa maqhama a lik'hemik'hale ka li-silane coupling agents le thepa ea bohlokoa ea 'mele joalo ka botsitso ba mocheso, botsitso ba sebopeho, le ho hanyetsa kutu - ho netefatsa ts'ebetso e tšoarellang halelele libakeng tse thata.