Agbara giga PTFE ti o ni iwọn otutu ti o ga julọ jẹ apapo ti gilaasi gilaasi giga ati PTFE ti a bo. Awọn ohun elo bọtini ni gbigbe gbigbe ile-iṣẹ (ndin ounjẹ, gbigbe asọ, gbigbe PCB), aabo alurinmorin (awọn ideri-ooru, awọn apata spatter), didimu ati dida titẹ gbona (iṣatunṣe roba, lamination PV), idabobo itanna (awọn ẹrọ iho moto, awọn wiwu okun), awọn membran ayaworan (awọn papa papa papa, 30+ igbesi aye ọdun), awọn isẹpo kemikali (apata-apa-apa-aaye), awọn ohun elo igbona gbigbona. awọn ibora), ati awọn ohun elo pataki (ige laser, titẹ sita 3D).

Gbigbe jẹ igbesẹ to ṣe pataki ni iṣelọpọ aṣọ iwọn otutu giga PTFE. Awọn abawọn ti o wọpọ pẹlu: fifọ (gbigbe ti o yara ju, awọ-ara oju-ara), iṣipopada ti a bo (awọn patikulu gbe si oju, alailagbara ti inu), awọn pinholes / roro (afẹfẹ idẹkùn tabi nyanu), awọn aaye funfun ati chalking (migration surfactant or incomplete fusion), yellowing/coking (overheating of additives), delamination (shrinkage stress over adhesion), (warpageven dry surface), osan peelkage inu ilohunsoke tutu (awọ ọrinrin awọn ẹgẹ), ati awọn egbegbe ti o nipọn (ipa-oruka kofi). Awọn ojutu kan pẹlu awọn profaili gbigbẹ iṣakoso ti iṣakoso, fentilesonu to dara, ati itọju sobusitireti.

PTFE emulsion impregnation ti fiberglass fabric nilo ọpọlọpọ awọn oluranlọwọ lati ṣaṣeyọri ibora aṣọ, ifaramọ ti o lagbara, ati awọn aaye ti ko ni abawọn. Awọn afikun bọtini ni: awọn aṣoju wetting (dinku ẹdọfu oju, mu ilaluja), awọn ohun ti o nipọn (viscosity iṣakoso ati iwuwo ti a bo), awọn olutọsọna pH (imuduro emulsion ni pH 9-10), awọn aṣoju asopọ silane (imudara ifaramọ si gilasi), awọn oluranlọwọ ti fiimu (PFA / FEP fun sintering), awọn olutọpa iṣẹ-ṣiṣe, awọn olutọpa pipọ (wearho) humectants (o lọra gbigbe). Aṣayan da lori sobusitireti ati awọn ibeere iṣẹ.

Aṣọ fiberglass ti o gbooro (aṣọ okun olopobobo) yato ni ipilẹṣẹ lati aṣọ gilaasi ti aṣa ni eto yarn. Nipasẹ itọju ọkọ ofurufu ti o ga-titẹ, awọn filaments gilasi ti nlọsiwaju ti wa niya, crimped, ati fluffed sinu voluminous, owu-bi owu. Eyi ṣẹda ti o nipọn, asọ ti o rọra pẹlu idabobo igbona ti o ga julọ (awọn ipele afẹfẹ idẹkùn), ibaramu ti o dara julọ, ṣiṣe imudara ti o ga julọ, ati imudara omije / fifẹ resistance - ni idiyele ti agbara fifẹ kekere diẹ. Ti a lo fun awọn gasiketi iwọn otutu giga, awọn ipari paipu, awọn baagi àlẹmọ, ati awọn edidi adiro.

Iwa mimọ ohun elo aise jẹ ipilẹ ti iṣẹ ṣiṣe ti iwọn otutu otutu PTFE. Emulsion PTFE ti o ga julọ (ko si awọn ions irin, ko si awọn iṣẹku iwuwo kekere-molekula) ṣe idaniloju resistance ooru (ko si yellowing soke si 260 ° C), iduroṣinṣin ti kii-stick, ati agbara dielectric giga. Fun gilaasi gilaasi, E-gilasi ti ko ni alkali (Na₂O <0.8%) n ṣetọju agbara ati idabobo ni awọn iwọn otutu giga; gilasi alabọde / giga-alkali nfa ibajẹ. Iyọkuro pipe ti awọn aṣoju iwọn wihun ṣe idilọwọ carbonization ati delamination. Iwa mimọ taara ni ipa lori igbesi aye iṣẹ, ibamu-ite ounje, ati igbẹkẹle itanna.

Gbigbe iṣaaju ti o yẹ ti aṣọ gilaasi jẹ pataki fun ibora PTFE ti o tẹle, impregnation resini, tabi lamination. Awọn itọju akọkọ mẹta: yiyọ ọrinrin ni 105-120 ° C (10-30 min da lori iwuwo), dewaxing / mimọ gbona ni 300-450 ° C (LOI <0.1%, yago fun> 500 ° C), ati preheating ni 60-100 ° C ṣaaju ki o to bo. Ṣakoso iṣọkan adiro otutu adiro (± 5°C), fi agbara mu dehumidification, ati aabo awọn aṣọ ti a ṣe itọju silane ni isalẹ 110°C. Tọju aṣọ ti o gbẹ sinu awọn baagi ti a fi edidi tabi awọn yara gbigbẹ (<30°C, <40% RH).

Aṣọ iwọn otutu giga PTFE (figilaasi ti a bo PTFE) ti fẹrẹẹ jẹ inert kemikali, ṣugbọn awọn nkan kan fa ibajẹ labẹ awọn ipo kan pato. Ikọlu PTFE taara waye pẹlu awọn irin alkali didà (sodium, potasiomu), awọn aṣoju fluorinating ti o lagbara (F₂, ClF₃) ni awọn iwọn otutu giga, ati didà alkalis lagbara loke 300°C. Ipata aiṣe-taara n ṣẹlẹ nigbati hydrofluoric acid (HF), alkalis ti o ni idojukọ gbona, tabi phosphoric acid gbona wọ inu awọn abawọn ibora ati kọlu sobusitireti fiberglass. Fun iṣẹ kẹmika to gaju, lo fiimu PTFE mimọ laisi gilaasi.

PTFE ga-otutu fabric (PTFE-coated fiberglass) ni o ni o tayọ gbona mọnamọna resistance laarin awọn oniwe-deede iṣẹ ibiti o ti -70°C to 260°C. O le fi aaye gba gigun kẹkẹ otutu otutu, fun apẹẹrẹ, gbigbe lati firisa -50°C si titẹ gbigbona 260°C. Awọn onipò Ere paapaa yege itutu agbaiye lojiji lati 260°C sinu omi 10°C. Bibẹẹkọ, awọn ohun elo iyalẹnu lati awọn iwọn otutu ti o ga ju 300°C (nitosi aaye yo PTFE's 327°C) yoo fa fifalẹ lẹsẹkẹsẹ ati delamination. Sobusitireti fiberglass pese iduroṣinṣin iwọn; ti a bo PTFE jẹ ipin idiwọn.

Aṣọ iwọn otutu giga PTFE ni lilo pupọ ni ile-iṣẹ kemikali fun awọn ohun elo bọtini meje: awọn gasiketi flange ati awọn paipu paipu (koju awọn acids / alkalis lagbara), riakito ati awọn ohun elo ojò (idilọwọ ipata irin, mimọ irọrun), awọn baagi àlẹmọ fun gaasi ibajẹ ibajẹ (to 260 ° C), awọn isẹpo imugboroja ipata fun awọn ducts, anti-adhesion, itusilẹ itanna / ifasilẹ atijọ, itusilẹ itanna idabobo murasilẹ. FDA ati UL onipò wa.

PTFE ga-otutu fabric (PTFE-ti a bo fiberglass) nfun mẹrin bọtini anfani bi ohun egboogi-ibajẹ ikan: kemikali inertness (koju aqua regia, lagbara alkalis, solvents), jakejado otutu ibiti o (-70 ° C to 260 ° C lemọlemọfún, 350 ° C tente oke), onisẹpo iduroṣinṣin (<0.5% kọ elongation), ati idena dada iduroṣinṣin. Ti a lo ninu awọn opo gigun ti kemikali, awọn ile-iṣọ desulfurization, awọn tanki gbigbe, ati ohun elo ounjẹ/pharma. FDA onipò wa.