Calendering – ntama a wɔde PTFE akata so a wɔde mia ahwehwɛ rollers a ɛyɛ hyew ntam wɔ 360-380°C – sesa ɔfasu no nsɛso kɛse, nea ɛma wogyae, sɛnea ɛmma nsu ntumi nkɔ mu, ne mfiridwuma mu adwumayɛ. Ɛtew roughness so fi Ra 0.5-1.0 μm kosi <0.05 μm, ɛto pinholes, ɛma sɛnea ɛko tia ɔsɛe no tu mpɔn, nanso ɛtew tetew ahoɔden ne sɛnea ɛyɛ mmerɛw so. Ɛho hia ma release liners ne anyinam ahoɔden insulation.

Fiberglass weave pattern – plain, twill, anaa satin – nya PTFE ntama a ɛyɛ hyew kɛse no su so nkɛntɛnso kɛse. Satin weave ma ahoɔden a ɛkorɔn sen biara a wɔtetew (2-3x plain) ne flexibility, a eye ma dynamic bending. Plain weave ma dimensional stability a eye sen biara ne peel adhesion, a ɛfata ma static applications. Twill kari pɛ wɔ agyapade nyinaa mu ma wɔde di dwuma wɔ ɔkwan a ɛkɔ akyiri so.

Nneɛma anan na ɛkyerɛ PTFE ntama a ɛyɛ hyew a ɛkorɔn a wɔde kata so pɛpɛɛpɛ: nea wɔde kata so (particle size 0.15-0.35 μm, viscosity, solid content), coating & sintering process (blade coating a wɔpɛ ma biakoyɛ), substrate su (weave pattern, pre-treatment), ne production environment (20-25°C, <60% RH). Dip + blade a wɔaka abom nhyehyɛe no kari pɛ wɔ penetration ne surface smoothness.

PTFE ntama a ɛyɛ hyew kɛse ma nnuru a ɛyɛ soronko a ɛko tia, na egyina acid a ano yɛ den, alkalis, organic solvents, ne mframa a ɛporɔw ano. Saa asɛm yi ka nneɛma a ɛko tia, anohyeto ahorow (alkali dade a ayow, nneɛma a ano yɛ den a ɛma fluorin), ne nneɛma atitiriw te sɛ ɔhyew, sɛnea ɛdɔɔso, ne mfiri mu nhyɛso ho asɛm kɔ akyiri.

Sɛ́ obi a ɔyɛ PTFE ntama a ɛyɛ hyew kɛse no, Jiangsu Aokai New Materials ma wunya adwumayɛfo nhumu. Botae titiriw a ɛwɔ fiberglass soro ayaresa mu ne sɛ wɔbɛkyekye molecule bridge a ɛda inorganic fiberglass ne organic PTFE ntam, sɛnea ɛbɛyɛ a wobesiesie wɔn inc