Nkan yii ni wiwa awọn iṣẹ ti PTFE ni idabobo igbona fun awọn ẹrọ misaili. Awọn ọna ṣiṣe mẹrin: jijẹ endothermic - PTFE depolymerizes ni ~ 400 ° C si tetrafluoroethylene (ifihan endothermic giga, ~ 3,000 ° C ifihan gaasi ijona), gbigba ooru nla ati yiyọ agbara igbona lati oju odi. Transpiration itutu ati gaasi fiimu idabobo - jijẹ gaasi (tetrafluoroethylene) permeate ita nipasẹ bulọọgi-pores, yọ dada ooru; Fiimu gaasi ti nṣàn ya sọtọ gaasi ijona otutu otutu lati odi, idinku isun ooru ti o sunmọ-ogiri nipasẹ> 50%; gaasi fiimu modifies aala Layer iyara / iwọn otutu, alleviating patiku ogbara.

Nkan yii ni wiwa awọn ohun elo ti Teflon aṣọ otutu otutu (PTFE-coated fiberglass fabric) ni aaye aerospace. Awọn agbegbe ohun elo bọtini: iṣelọpọ ohun elo idapọmọra - itusilẹ asọ / fiimu ni idọti autoclave, awọn ipele ipinya, awọn beliti gbigbe iwọn otutu giga fun iṣelọpọ prepreg; Enjini ati aabo igbona otutu-giga - awọn ibora idabobo igbona, didi ogiriina, awọn asopọ iwọn otutu to rọ; Itanna idabobo ati waya ijanu Idaabobo - USB murasilẹ ni engine compartments ati ibalẹ jia bays; Awọn inu inu ọkọ ofurufu ati aabo ina - awọn aṣọ-ikele ina / awọn idena ẹfin ti o ni ibamu pẹlu awọn iṣedede FST, ibora ibora gbona / akositiki; Awọn aaye ati awọn ohun elo aerospace - awọn apejọ ọpọ-Layer idabobo (MLI), awọn ila-iṣan lubrication anti-tutu-weld fun awọn ilana imuṣiṣẹ ti oorun ati awọn mitari eriali, asọ iṣakoso gbona.

Nkan yii ṣe itupalẹ bii iyanrin tabi itọju ipari matt ṣe ni ipa lori eto dada ti asọ iwọn otutu giga PTFE. Awọn ayipada waye ni awọn iwọn mẹta: Mofoloji airi yipada lati didan digi-bi si sojurigindin gully ti o ni inira pẹlu awọn iye Ra / rz ti o pọ si, ṣiṣẹda awọn ẹya ara ẹrọ anchoring 3D fun isọpọ atẹle. Iduroṣinṣin ti a bo dojukọ awọn ewu: PTFE Layer thinning, ifihan agbara ti sobusitireti fiberglass (nfa isonu ti ohun-ini ti kii ṣe igi, ilaluja ọrinrin, ati agbara ẹrọ ti o dinku), pẹlu awọn microcracks ati iran idoti.

Nkan yii ṣafihan ilana ipilẹ ti o pe fun impregnating fiberglass fabric pẹlu emulsion PTFE. Awọn igbesẹ bọtini meje: ① Pretreatment (dewaxing/desizing) ni 350-400°C lati yọ awọn aṣoju wiwọn aṣọ; ② Ilana Emulsion pẹlu 40-55% akoonu ti o lagbara ati awọn surfactants fun imudara wetting; ③ Impregnation nipasẹ ọna dip-squeeze tabi ibora abẹfẹlẹ dokita; ④ Gbigbe ni 100-150 ° C lati rọra yọ omi kuro ki o si ṣe fiimu PTFE ti o gbẹ; ⑤ Sintering ni 360-390 ° C (titi di 400 ° C) lati yo awọn patikulu PTFE sinu fiimu ti o tẹsiwaju; ⑥ Multi-cycle impregnation-gbígbẹ-sintering tun 2-4 igba lati de ọdọ afojusun sisanra ati resini akoonu (45-65%); ⑦ Itọju lẹhin-itọju pẹlu itọju corona, gige eti, yikaka ati ayewo didara. Awọn aaye iṣakoso koko: dewaxing pipe, rirọ emulsion ni kikun, gbigbe mimu mimu, iwọn otutu sintering deede, ati iwuwo bora deede. Awọn ọja sin ga-igbohunsafẹfẹ Ejò-agbada laminates, ga-otutu conveyor beliti ati ayaworan awọn ohun elo awo.

Finifini imọ-ẹrọ yii lati Jiangsu Aokai ṣe itupalẹ bawo ni iwọn kekere ti o pọ ju tabi awọn iwọn otutu sintering giga ṣe ba asọ iwọn otutu giga PTFE jẹ. Irẹwẹsi kekere fi awọn patikulu silẹ ti ko ni yo, ti o nfa awọn pores bulọọgi, isomọ sobusitireti ti a ko lagbara, awọn ibi-afẹfẹ ti o ni inira, agbara ẹrọ ti ko dara, ati irisi akomo wara. Overheating induces PTFE ooru ibaje, ti o npese pinholes, nyoju, brittleness, ofeefee-si-dudu discoloration, ati dasile oloro èéfín. Awọn iwọn mejeeji ṣe iparun iwapọ, iṣẹ ti kii ṣe igi, irọrun, idabobo, ati iduroṣinṣin iwọn.

Calendering – titẹ PTFE-ti a bo fabric laarin kikan digi rollers ni 360-380 ° C – bosipo paarọ dada mofoloji, Tu-ini, impermeability, ati darí iṣẹ. O dinku roughness lati Ra 0.5-1.0 μm si <0.05 μm, edidi awọn pinholes, ṣe ilọsiwaju resistance resistance, ṣugbọn dinku agbara omije ati irọrun. Pataki fun awọn laini idasilẹ ati idabobo itanna.

Gẹgẹbi olupilẹṣẹ ọjọgbọn ti awọn aṣọ iwọn otutu giga PTFE, Awọn ohun elo Tuntun Jiangsu Aokai fun ọ ni awọn oye ọjọgbọn. Idi pataki ti itọju dada fiberglass ni lati kọ afara molikula laarin gilaasi inorganic ati PTFE Organic, lati le yanju ipilẹṣẹ inc inc ti ara wọn.