O lenei tusiga o loʻo aofia ai faʻaoga o le Teflon maualuga-vevela ie (PTFE-coated fiberglass fabric) i totonu ole vateatea. Vaega autu o le faaaogaina: gaosiga o meafaitino tuufaatasi - tatala ie / ata tifaga i autoclave molding, tulaga tuufua, maualuga-vevela conveyor fusi mo prepreg gaosiga; Inisinia ma le maualuga o le vevela puipuiga - palanikeke insulation vevela, puipui puipui, fetuutuunai sootaga maualuga-vevela; Puipuiga fa'aeletise ma fa'amau uaea - afifi uaea i totonu o vaega afi ma faga o mea e tu'u ai; Va'alele totonu ma puipuiga afi - pupuni afi/asu pa pupuni e fetaui FST tulaga, vevela/acoustic insulation palanikeke ufiufi; Avanoa ma aerospace talosaga - faʻapipiʻi faʻapipiʻi faʻapipiʻi (MLI), faʻapipiʻi lubrication anti-cold-weld mo masini faʻapipiʻiina o le la ma faʻamau antenna, ie e pulea ai le vevela.

O lenei tusiga o loʻo faʻamatalaina pe faʻafefea ona faʻapipiʻiina e le PTFE le fusipaʻu i le fiberglass ie substrate i Teflon ie vevela maualuga. E le mafai ona fa'apipi'i fa'ama'i tu'usa'o ona o le malosi ole maualuga ole PTFE. Fa'amauina e maua e ala i le: Fa'afeso'ota'i fa'ainisinia (fa'apipi'i fa'aletino) - E ulu le emulsion o le PTFE i va alava ma u'u fusi fa'aalava pe a uma ona sintering; Silane so'o fa'apipi'i muamua togafiti - fa'atūina le alalaupapa mole i le va o alava tioata fa'a-organic ma fa'ameamea; Laega suiga muamua o vaila'au - fa'aaoga PAI, PPS, PES po'o PEEK resins ma le PTFE micropowder, fa'aoga pe a mae'a togafitiga fa'apipi'i e fa'atupu ai le malosi o le suiga; Lamination ata fa'apipi'i vevela - FEP po'o ata PFA (mea fa'afefeteina 260-310°C) fa'apipi'i muamua ata tifaga PTFE i ie; Fa'asologa fa'asolosolo e ala i le tele o le impregnation ma le sintering cycles - fa'afefeteina le pasi muamua ma le fusifusia / so'o fa'apipi'i e ulu loloto i alava, soso'o ai ma mama PTFE impregnations, fatuina gradient compositional mai fiberglass i PTFE mama.

O lenei tusiga o loʻo faʻamatalaina pe faʻafefea ona faʻapaleniina e le mamanu fausaga microporous o le Teflon mānava (PTFE) le vevela maualuga le faʻaogaina o le ea ma mea faʻamama ma mea e le faʻapipiʻi. Fete'ena'iga autu: e mana'omia le fa'aogaina o le ea pores matala, a'o le fa'amama e mana'omia le mafiafia ma e le pipi'i e mana'omia ni mea lamolemole. Fuafuaga fuafuaina paleni: pulea averesi pore diameter (0.1-2μm, lelei <0.5μm) e puipuia ai liusua ulu ma faatumauina le gau gau; pulea porosity i 50-70% (≈60% sili ona lelei) ausia Gurley 20-100s/100cc ma dielectric malosi ≥2kV mo 0.13mm ata tifaga; fa'aogaina le fa'aogaina o pupuni feso'ota'iga 3D maualuga (τ≈2.5-4) e taofiofia ai ala lafoa'i sa'o; fau le fausaga o pore gradient asymmetric fa'atasi ma le mafiafia o le pa'u o le pa'u (1-5μm) mo le le fa'apipi'i/fa'a'ese'ese ma totonu porous mo le manava; fa'aaoga le super-oleophobic/hydrophobic i luga o le fa'agata pe a mae'a togafitiga e aunoa ma se pupuni pupuni.

O lenei tusiga o loʻo tuʻuina atu ai fofo faʻapitoa mo le puipuia o toega pipii ma le pipii toto pe a faʻaaogaina le PTFE maualuga-vevela lipine e puipuia ai PCB auro tamatamailima i le taimi o le fono SMT. Su'esu'ega o a'a: o mea o totoe e tupu mai i le fa'aletonu o le tu'ufa'atasi po'o le fa'afeso'ota'i; e tupu mai le toto ona o le pa'u viscosity ma le sosolo i lalo ole vevela. Fofo autu o le filifiliga lipine talafeagai: silicone PSA ma taimi pupuu tumutumu ≥300°C, faaauau pea ≥260°C, atoa mafiafia 0.08-0.13mm ma mea manifinifi maualuga-cohesion adhesive layers, ma anti-toto/toega-saoloto tusi faamaonia. Pulea faiga e ono-laasaga: fa'amamāina a'o le'i lamination i le IPA; lamination zero-tension fa'atasi ai ma le fa'asao atoatoa o le ea; fa'alelei fa'alelei fa'amatalaga o le vevela ma le fa'amafanafana mālū (<2°C/s); pa'u malulu i lalo ole 50°C ile 180° angle; fa'agaioiina vave i totonu ole 24 itula ma na'o le fa'aoga tasi; fa'aletonu le fa'aogaina o le IPA solo ma le 40-50x su'esu'ega fa'alautele. Mo PCB e lua itu, sui i le lipine fou a'o le'i faia le itu lona lua.

O lenei tusiga o loʻo tuʻuina atu ai taʻiala faʻapitoa i le puipuia o maanuminumi ile PTFE ie vevela maualuga ile taimi ole sintering. Maanuminumi e mafua ona o le le tutusa o le vevela ma le faʻalavelave faʻalavelave. O vaifofo e aofia ai le fa'aogaina atoa o galuega: fa'atonuga o meafaitino mata (fa'ato'a atuaxing/vevela fa'atulagaina e fa'aumatia ai le fa'alavelave i totonu); impregnation ma faʻamago (tele faʻapipiʻi manifinifi, faʻafefete malie vevela, taʻavale malosi); pulea ogaumu sintering (1-3% overfeed mo alauni shrinkage vevela, tapuni tapuni micro-tension pulea, transverse vevela uniformity i totonu ± 5°C, gradient preheating-sintering-maalili curve, ogaumu ea-flotation o se fofo sili ona lelei, curved spreader rollers); fa'alili ma fa'atūina (fa'alili fa'agesegese, fa'atumauina le sosolo se'ia o'o i lalo ifo o le 100°C, fa'amalie atoa a'o le'i fa'avili); mata'ituina i luga ole laiga ma su'esu'ega malamalama malosi ma su'esu'ega infrared.

O lenei tusiga o loʻo aofia ai manaʻoga fua faatatau malulu i le taimi o le sintering ie vevela maualuga o le PTFE. A maeʻa le sintering i le 380-400 ° C, o le ie e tatau ona vave pasia le 310-315 ° C crystallization-sensitive zone. Ole fua ole fa'amalieina fautuaina e le itiiti ifo i le 30-50 ° C / min (ie manifinifi e mafai ona ausia le 100-200 ° C / min e ala i le malulu o le ea). Faʻafefe vave (tineia) e maua ai le tioata maualalo (45-50%), faʻamaluluina, faʻafefeteina maaa ma lamolemole luga, faʻapipiʻi malosi, sili ona lelei e le faʻaogaina, ma le tetee i le delamination ma le taʻe. O le fa'alili lemu (fa'alili o le ogaumu) e maua ai le maualuga o le tioata (60-70%), ma mafua ai ona ma'a'a, fa'apalapala ma'ale'ale e fa'afefete, pa'u ma microcracks.

O lenei tusiga e faʻatusatusa ai le vevela o le potu ma le maualuga o le vevela o le faʻapipiʻi faʻapipiʻi silikoni mo le lipine PTFE. O le matua maualuga o le vevela (120-180°C) e fa'atupuina ai feso'ota'iga mafiafia e feso'ota'i fa'atasi ai ma le malosi fa'atasi, e puipuia ai le to'ega pipii pe a uma ona pa'u. E fausia ai fusi fa'ama'i fa'ama'i fa'atasi ma substrates PTFE e ala i le fa'amoma'i fa'atasi muamua, fa'aitiitia ai a'afiaga o le delamination. O le matua maualuga o le vevela e aveese ai foʻi mea vaivai mole mole aʻo leʻi tuʻuina atu, puipuia ai le faʻafefe ma le faʻaleagaina o le suauʻu silicone i le taimi muamua o le faʻamafanafanaina.

O lenei ta'iala o lo'o aofia ai le filifilia o lipine fa'amau maualuga a le PTFE mo le fa'aogaina o le tui ma le fa'aogaina o le fa'apipi'i. Filifiliga faʻavae vevela: ≤260 ° C mo palasitika lautele (silikoni PSA masani, 0.13-0.18mm); 260-300 ° C mo palasitika inisinia maualuga-vevela pei PC, PA66, POM (maualuga silicone pipii, 0.18-0.25mm); 300-400°C mo PEEK, LCP, PPS latalata i tamo'e vevela (fa'apipi'i fa'apipi'i le manuia; fa'aoga ie PTFE e leai se pipii po'o le ata PFA). Filifiliga fa'avae: mea tacky mana'omia maualuga-fa'asa'oloto luga PTFE mama; tioata / minerale tumu mea e manaʻomia le mamafa-tiute 0.25mm + ofuina-tetee lipine; mea fa'apipi'i fa'ama'i e mana'omia se mea fa'apipi'i fa'ama'i ma mea mafiafia; talosaga ma'ale'ale mana'omia anti-static lipine PTFE uliuli.

O le ie maualuga o le PTFE maualuga e faia e ala i le ufiufi o le PTFE i luga o le ie fiberglass malosi, ofoina atu le malosi faʻamalosi, faʻafefe vevela, mea e le faʻapipiʻi, vailaʻau faʻamaʻi, ma le maualalo o feteʻenaʻiga. Fa'aoga autu e aofia ai: felauaiga fa'apisinisi (fa'amago vevela, tao tao mea'ai, fa'amago ie, fa'agogo pepa/tifiti); ie tu'u fa'amuta fa'apalapala ma fa'alava aluga lomi vevela; u'uina pupuni puipui ma peleue fa'amama vevela; afi eletise ma le fa'anofoina o le transformer; fale fa'ase'e ma lagolago paipa; filtration vailaʻau ma faʻamaufaʻailoga valve i siosiomaga corrosive. O le malosi maualuga e fa'amautinoa ai le tumau i lalo o le vevesi, saeia, fa'asolo pea, ma le maualuga o le vevela fa'ainitaneti i luga o nei fa'aoga mamafa-tiute eseese.

I le taimi o le sintering, o vaega o le PTFE i luga o le ie fiberglass ua liusuavai i luga aʻe o le 327°C, faʻaumatia ai lamellae gaugau-laina muamua ma tuaoi o vaega e fausia ai se liusuavai amorphous. I luga o le mālūlūina, toe fa'ama'a'aina le PTFE i spherulites e aofia ai lamellae fa'ata'ita'i, fa'atasi ai ma tioata e 50-70%. Ole fua ole malulu e iloa ai le atoatoa o tioata: faʻagesegese le malulu e maua ai le tioata maualuga, spherulites tetele, sili atu le maaa; tineia vave e maua ai spherulites sili atu ona lelei ma faaleleia fetuutuunai.