Hoʻopili kēia ʻatikala i ka hoʻohana ʻana i ka lole wela kiʻekiʻe ʻo Teflon (PTFE-coated fiberglass fabric) ma ke kahua aerospace. Nā wahi noi nui: ʻO ka hana ʻana i nā mea hana - hoʻokuʻu i ka lole/kiʻiʻoniʻoni i loko o ka hoʻoheheʻe autoclave, nā papa kaʻawale, nā kāʻei conveyor wela kiʻekiʻe no ka hana prepreg; ʻEnekini a me ka wela wela kiʻekiʻe - nā pākeʻe insulation thermal, pale ahi, nā pilina wela kiʻekiʻe maʻalahi; ʻO ka hoʻokaʻawale uila a me ka pale ʻana i ke kaula uwea - ka ʻōwili ʻana i ke kaula i loko o nā keʻena ʻenekini a me nā kaʻa pae ʻāina; ʻO loko o ka mokulele a me ka pale ahi - nā pale ahi / nā pale uahi e kū ana i nā kūlana FST, ka uhi ʻana i ka pale pale wela/acoustic insulation; Nā noi ākea a me nā aerospace - nā hui hoʻohuihui multi-layer (MLI), anti-cold-weld lubrication liners no nā mīkini hoʻoneʻe solar panel a me nā hinges antenna, nā lole hoʻomalu wela.

Hōʻike kēia ʻatikala pehea ka hoʻopaʻa ʻana o ka PTFE i nā mea hoʻopaʻa lole fiberglass i ka lole wela kiʻekiʻe ʻo Teflon. ʻAʻole hiki ke hoʻopaʻa kemika pololei ma muli o ka ikehu ʻili o ka PTFE. Loaʻa ka hoʻopaʻa ʻana ma o: Mechanical interlocking (physical bonding) — PTFE emulsion ke komo i nā ʻāpana fiber a hoʻopaʻa i nā puʻupuʻu fiber ma hope o ka sintering; ʻO ka hoʻomaʻamaʻa mua ʻana o ka mea hoʻohui Silane - hoʻokumu i ke alahaka molekala ma waena o nā fiber aniani inorganic a me ka primer organik; ʻO ka papa hoʻololi mua kemika - me ka hoʻohana ʻana i nā resins PAI, PPS, PES a i ʻole PEEK me ka micropowder PTFE, i hoʻohana ʻia ma hope o ka hoʻopili ʻana i ka lāʻau e hana i ka papa hoʻololi ikaika; Lamination kiʻiʻoniʻoni hoʻoheheʻe wela - FEP a i ʻole PFA kiʻiʻoniʻoni (kahi hoʻoheheʻe 260-310 ° C) i hoʻopaʻa mua ʻia nā kiʻiʻoniʻoni PTFE i ka lole; ʻO ka hoʻolālā gradient ma o ka nui o ka impregnation a me ka sintering cycles - dilute first pass me ka binder/coupling agent e komo hohonu i loko o nā fibers, a ukali ʻia e nā impregnations PTFE maʻemaʻe, e hana ana i ka gradient haku mele mai fiberglass a PTFE maʻemaʻe.

Kūkākūkā kēia ʻatikala pehea ka hoʻolālā ʻana o ka microporous structure o breathable Teflon (PTFE) kiʻekiʻe-mehana tape ke kaulike i ka ea me ka insulation a me ka waiwai ʻole. ʻO ka hakakā kumu: pono ka ʻae ʻana o ka ea i nā pores hāmama, ʻoiai ke koi nei ka insulation i ka density a me ka non-stick e pono ai i nā ʻili laulima. Nā hoʻolālā hoʻolālā kaulike: e hoʻomalu i ke anawaena pore awelika (0.1-2μm, kūpono <0.5μm) e pale i ka hoʻoheheʻe ʻana a mālama i ka puʻupuʻu haʻihaʻi; e hoʻomalu i ka porosity ma 50-70% (≈60% maikaʻi) e loaʻa ana iā Gurley 20-100s / 100cc a me ka ikaika dielectric ≥2kV no ke kiʻi 0.13mm; e hoʻohana i ke ʻano pore network 3D kiʻekiʻe-tortuosity (τ≈2.5-4) e hoʻopaʻa i nā ala hoʻokuʻu pololei; kūkulu i ka ʻano pore gradient asymmetric me ka ʻili ʻili o ka ʻili (1-5μm) no ka non-stick/insulated a me ka porous i loko no ka hanu; e hoʻohana i ka super-oleophobic/hydrophobic surface post-treatment me ka ʻole o ka paʻa ʻana o ka pore.

Hāʻawi kēia ʻatikala i nā ʻōnaehana hoʻonā no ka pale ʻana i ke koena adhesive a me ke koko adhesive i ka wā e hoʻohana ai i ka tape wela kiʻekiʻe PTFE e pale i nā manamana gula PCB i ka wā o ka hui SMT. Ka nānā ʻana i ke kumu kumu: loaʻa mai ke koena mai ka hāʻule ʻole ʻana a i ʻole ka hoʻololi ʻana o ke alo; hiki mai ke koko mai ka hā'ule'ana o ka viscosity a me ke kahe o ka mea ho'opili ma lalo o ka wela hou. ʻO ka hopena koʻikoʻi ke koho lipine kūpono: silicone PSA me ka wā pōkole ≥300 ° C, hoʻomau ≥260 ° C, ka mānoanoa holoʻokoʻa 0.08-0.13mm me nā papa adhesive kiʻekiʻe-cohesion, a me ka hōʻoia anti-bleed / koena ʻole. ʻEono kaʻina kaʻina hana: hoʻomaʻemaʻe mua-lamination me IPA; zero-tension lamination me ka hoʻokuʻu ʻana i ka ea piha; ʻO ka hōʻike ʻana i ka mahana hoʻihoʻi maikaʻi ʻia me ka hoʻomehana mālie (<2°C/s); ʻili anuanu ma lalo o 50 ° C ma ke kihi 180 °; ka hana koke ʻana i loko o 24 mau hola a hoʻohana hoʻokahi wale nō; ka hoʻohana ʻole ʻana me ka holoi ʻana i ka IPA a me ka nānā ʻana i ka mea hoʻonui 40-50x. No nā PCB ʻaoʻao ʻelua, e hoʻololi me ka lipine hou ma mua o ka hana ʻana i ka ʻaoʻao ʻelua.

Hāʻawi kēia ʻatikala i ke alakaʻi ʻōnaehana no ka pale ʻana i nā wrinkles ma ka PTFE kiʻekiʻe-mehana lole i ka wā sintering. ʻO nā wrinkle ke kumu ma muli o ka emi ʻana o ka wela a me ke kaumaha ʻole. Hoʻopili nā mea hoʻonā i ke kahe hana piha: ka mana substrate maka (hoʻopau dewaxing / hoʻonohonoho wela e hoʻopau i ke koʻikoʻi o loko); ka impregnation a me ka maloʻo ʻana (nā ʻāpana lahilahi he nui, ke aniani wela haʻahaʻa, nā wili holo ikaika); ka hoʻomalu ʻana i ka umu ahi (1-3% overfeed no ka hāʻawi ʻana i ka wela, ka hoʻopaʻa ʻana i ka micro-tension control, transverse temperature uniformity i loko o ± 5°C, gradient preheating-sintering-cooling curve, air-flotation furnaces e like me ka hopena maikaʻi loa, curved spreader rollers); ka hoʻoluʻu a me ka hoʻonohonoho ʻana (hoʻolili mālie, mālama i ka pālahalaha ʻana a hiki i lalo o 100 ° C, hoʻomaha piha ma mua o ka wili ʻana); ka nānā pūnaewele me ka nānā māmā ikaika a me ka nānā ʻana i ka infrared.

Hoʻopili kēia ʻatikala i nā koi o ka hoʻomaha ʻana i ka wā PTFE kiʻekiʻe-mehana lole sintering. Ma hope o ka sintering ma 380-400 ° C, pono ka lole e hele wikiwiki i ka 310-315 ° C crystallization-sensitive zone. ʻO ka nui o ka hoʻoluʻu ʻōlelo ʻia he 30-50°C/min (hiki i ka lole lahilahi ke loaʻa i ka 100-200°C/min ma o ka hoʻoluʻu ea). ʻO ka hoʻomaloʻo wikiwiki (quenching) e hoʻopuka i ka crystallinity haʻahaʻa (45-50%), e hāʻawi ana i ka palupalu a me ka paʻakikī me nā papa laulima, ka adhesion ikaika, ka maikaʻi ʻole o ka lāʻau, a me ke kūpaʻa ʻana i ka delamination a me ka haki. ʻO ka hoʻoluʻu lohi (ka hoʻoluʻu ʻana i ka umu) ka hopena i ka crystallinity kiʻekiʻe (60-70%), e hoʻopiʻi ai i ka paʻa ʻole a me ka palupalu a hiki ke emi, ka ʻili a me nā microcracks.

Hoʻohālikelike kēia ʻatikala i ka hoʻomaʻamaʻa ʻana o ka lumi-mehana a me ke kiʻekiʻe-mehana o ka mea hoʻopili paʻi koʻikoʻi silicone no ka tape PTFE. Hoʻokumu ka hoʻomaʻamaʻa wela kiʻekiʻe (120-180 ° C) i nā ʻupena crosslinked paʻa me ka ikaika cohesive ikaika, e pale ana i ke koena adhesive ma hope o ka ʻili ʻana. Hoʻokumu ia i nā mea hoʻopaʻa hoʻopaʻa kemika me nā substrates PTFE ma o ka co-curing primer, e hoʻopau ana i nā pilikia delamination. Hoʻopau pū ka maturation wela kiʻekiʻe i nā volatiles haʻahaʻa haʻahaʻa ma mua o ka lawe ʻana, e pale ana i ka huʻihuʻi a me ka ʻaila silicone i ka wā hoʻomehana mua.

Hoʻopili kēia alakaʻi i ke koho lipine kiʻekiʻe PTFE no ka hoʻoheheʻe ʻana i ka hoʻoheheʻe ʻana a me nā noi anti-stick. Koho ma muli o ka wela: ≤260°C no nā plastics maʻamau (ka lipine PSA silicone maʻamau, 0.13-0.18mm); 260-300°C no nā plastics ʻenekinia kiʻekiʻe e like me PC, PA66, POM (kiʻekiʻe-temp silicone adhesive, 0.18-0.25mm); 300-400°C no PEEK, LCP, PPS kokoke i nā kukini wela (ʻaʻole hiki ke hoʻopaʻa ʻia; hoʻohana i ka lole PTFE adhesive-free a i ʻole PFA film). Koho ma muli o nā mea waiwai: pono nā mea hoʻokuʻu kiʻekiʻe i ka PTFE maʻemaʻe; ʻO nā mea aniani/mineral i hoʻopiha ʻia e koi i ka lipine 0.25mm paʻa kaumaha; ʻO nā mea hoʻohui corrosive e koi i ka mea hoʻopili kemika a me ka substrate paʻa; Pono nā noi static-sensitive anti-static black PTFE tape.

Hana ʻia ka PTFE kiʻekiʻe kiʻekiʻe ma ka uhi ʻana i ka PTFE ma luna o ka lole fiberglass ikaika, hāʻawi i ka ikaika tensile, pale wela, nā waiwai non-stick, kūpaʻa kemika, a me ka haʻahaʻa haʻahaʻa. ʻO nā noi koʻikoʻi: ka lawe ʻana i ka ʻoihana (ka wela wela, ka kuke ʻana i ka meaʻai, nā mea maloʻo lole, ka maloʻo pepa/kiʻiʻoniʻoni); ʻO ka lole hoʻokuʻu hoʻoheheʻe hui a me nā liner cushion press wela; wiliwili i nā pale pale a me nā ʻaʻahu insulation thermal; kaʻa uila a me ka mea hoʻololi hoʻololi; ke kūkulu ʻana i nā bearings sliding a me nā kākoʻo pipeline; kānana kemika a me ka hoʻopaʻa ʻana i ka valve i loko o nā kaiapuni corrosive. ʻO ka ikaika tensile kiʻekiʻe e hōʻoia i ka lōʻihi ma lalo o ka haʻalulu, ka haehae ʻana, ka hoʻoluliluli pinepine ʻana, a me ke koʻikoʻi mechanical wela kiʻekiʻe ma waena o kēia mau noi kaumaha.

I ka wā o ka sintering, hehee nā ʻāpana PTFE ma ka lole fiberglass ma luna o 327°C, e luku ana i nā lamellae i pelu ʻia a me nā palena ʻāpana e hana i ka hehee amorphous. Ma ka hoʻoluʻu ʻana, hoʻihoʻi hou ʻia ka PTFE i loko o nā spherulites i haku ʻia me nā lamellae radially oriented, me ka crystallinity mai 50-70%. Hoʻoholo ka helu hoʻoluʻu i ka hemolele kristal: ʻoi aku ka nui o ka hoʻoluʻu ʻana i ka crystallinity, ʻoi aku ka nui o nā spherulites, ʻoi aku ka paʻakikī; ʻO ke kinai wikiwiki e hāʻawi i nā spherulites maikaʻi a hoʻomaikaʻi i ka maʻalahi.