Sehlogo se se lebane le ka moo tlhamo ya sebopego sa microporous sa theipi ya themperetšha ya godimo ya Teflon ye e hemago (PTFE) e lekalekanyago go tsenelela ga moya le dithoto tša go thibela go fiša le tšeo di sa kgomaretšego. Thulano ya motheo: go tsenelela ga moya go nyaka mašobana a bulegilego, mola go thibela go fiša go nyaka segokanyipalo le go se kgomarele go nyaka bokagodimo bjo bo boreledi. Maano a go hlama a lekalekanego: laola bophara bja pore bja karolelano (0.1-2μm, ka mo go swanetšego <0.5μm) go thibela go tsenelela ga melt le go boloka gagamalo ya go thubega; taolo porosity ka 50-70% (≈60% Optimum) finyella Gurley 20-100s / 100cc le dielectric matla ≥2kV bakeng sa 0.13mm filimi; amogela phahameng-tortuosity 3D marangrang pore sebopeho (τ≈2.5-4) ho hatella otlolohile-ka ho lokolloa metjha e; aga asymmetric gradient pore sebopeho le teteaneng bokagodimo letlalo lera (1-5μm) bakeng sa bao e seng khomarela / inulation le porous ka hare bakeng sa breathability; diriša super-oleophobic / hydrophobic bokagodimo ka morago ga kalafo ntle le pore thibelo.

Sehlogo se se tšweletša mehola ya lešela la themperetšha ya godimo ya PTFE bjalo ka methopo ya ditaba ya sefa ya themperetšha ya godimo. Matla a tshela a bohlokwa: Kganetšo ya themperetšha ye e tšwetšego pele (260°C ye e tšwelago pele, tlhora ~ 300°C), ye e fetago PPS (190°C) le aramid (200°C); Go se šome mo go feteletšego ga dikhemikhale kgahlanong le diesiti, di-alkali, disolvent le di-oxidant, go lwantšha hydrolysis, go feta aramid le P84 ka gare ga khase ya go tšhuma ye e bolago; Superior lerole hloekisa tshebetso le ultra-tlaase bokagodimo matla kgontsha bonolo lerole kuku ho tloswa le tšoarellang tlaase khatello ea theoha; Bokgoni bjo bobotse bja go sefa ka bogolo bja pore bja 0.1-3μm bjo bo swarago ka godimo ga 99.99% ya dikarolwana tša PM2.5; Go se tuka ka LOI ka godimo ga 95%, ka dikgetho tša go lwantšha go se fetoge tše di lego gona; Matla a godimo a metšhene go tšwa go maatlafatšo ya fiberglass, ka methopo ya ditaba ya tlhale ya PTFE ye e hlwekilego yeo e fago go fetofetoga le maemo le bophelo bja tirelo bja >4 mengwaga. E bapetša gabotse kgahlanong le PPS, aramid, Nomex, P84 le methopo ya ditaba ya filtara ya fiberglass go ralala le themperetšha, go ganetša dikhemikhale, go ganetša hydrolysis le tshepedišo ya go hlwekiša.

Sehlogo se se fa ditharollo tše di rulagantšwego tša go thibela mašaledi a sekgomaretši le go tšwa madi a sekgomaretši ge o šomiša theipi ya themperetšha ya godimo ya PTFE go šireletša menwana ya gauta ya PCB nakong ya kopano ya SMT. Tshekatsheko ya sebaki sa modu: mašaledi a direga go tšwa go go palelwa ga kgokagano goba phetišetšo ya segokanyimmediamentsi sa sebolokigolo; go tšwa madi go direga go tšwa go go theoga ga viscosity le go tlala ga sekgomaretši ka fase ga phišo ya reflow. Tharollo ya motheo ke kgetho ya theipi ye e swanetšego: silicone PSA ka tlhora ya nako ye kopana ≥300°C, ye e tšwelago pele ≥260°C, botenya bja palomoka bja 0.08-0.13mm ka magato a sekgomaretši a godimo a kgokagano ye sesane, le netefatšo ya go se be le madi/mašaledi. Taolo ya tshepedišo ya megato ye tshela: go hlwekiša pele ga lamination ka IPA; lefela-kgateletšego lamination le go hudušwa ga moya ka botlalo; optimized reflow mocheso profil le bonolo futhumatsang (<2 ° C / s); go ebola ka go tonya ka fase ga 50°C ka khutlo ya 180°; tshepedišo ya ka pela mo diiri tše 24 le tšhomišo e tee fela; go palelwa go swara ka IPA phumola le 40-50x magnifier tlhahlobo. Bakeng sa di-PCB tša mahlakore a mabedi, tšeela sebaka ka theipi ye mpsha pele ga tshepedišo ya lehlakore la bobedi.

Sehlogo se se fa tlhahlo ye e rulagantšwego ya go thibela megokolodi godimo ga lešela la themperetšha ya godimo ya PTFE nakong ya go sintering. Di- wrinkles motheong di bakwa ke go fokotšega mo go sa leka-lekanego ga phišo le kgateletšego e sa dumelelanego. Ditharollo di akaretša tshepedišo ya mošomo ka botlalo: taolo ya substrate ya didirišwa tše tala (dewaxing ye e feletšego/peakanyo ya phišo go fediša kgateletšego ya ka gare); impregnation le omisa (coatings tse ngata tšesaane, bonolo mocheso gradient, mafolofolo drive rollers); sintering sebjana taolo (1-3% overfeed bakeng sa mogote shrinkage kabelo, koaletsoeng-loop micro-kgateletšego taolo, transverse mocheso uniformity ka hare ho ± 5 ° C, gradient preheating-sintering-pholile koba, moea-phaphametse libebe e le tharollo Optimum, kobehileng spreader rollers); go fodiša le go beakanya (go tonya ka go nanya ganyenyane-ganyenyane, boloka go phatlalala go fihla ka tlase ga 100°C, go fodiša ka botlalo pele o sotha); go baya leitlho inthaneteng ka tlhahlobo e matla leseli le skena sa infrared.

Sehlogo se se sekaseka ka moo kalafo ya go thuthupiša ka santa goba ya go fetša ka matt e amago sebopego sa bokagodimo bja lešela la themperetšha ya godimo ya PTFE. Diphetogo di direga ka dikarolo tše tharo: Sebopego sa maekerosekopo se fetoga go tšwa go sebopego se se boreledi sa go swana le seipone go ya go sebopego sa moedi wo o makgwakgwa ka dikelo tša Ra/Rz tše di oketšegilego kudu, go hlola dibopego tša go tsenya ditshetledi tša motšhene tša 3D bakeng sa kgokagano ye e latelago. Botshepegi bja go tlotša bo lebane le dikotsi: Go sesafala ga legato la PTFE, go pepentšhwa mo go ka bago gona ga substrate ya fiberglass (go hlola tahlegelo ya thepa yeo e sa kgomaretšego, go tsenelela ga monola, le go fokotšega ga maatla a motšhene), gotee le microcracks le moloko wa ditlakala.

Sehlogo se se tsebagatša tshepedišo ya motheo ye e feletšego ya go kolobiša lešela la fiberglass ka emulsion ya PTFE. Megato ye šupa ya bohlokwa: 1 Kalafo ya pele (go tloša boka/go tloša bogolo) ka 350-400°C go tloša didirišwa tša go dira bogolo bja lešela; 2 Emulsion tlhamo le 40-55% dikahare tiileng le surfactants bakeng sa ntlafatsoa kolobiša; 3 Impregnation ka mokgwa wa dip-squeeze kapa ngaka legare tlotsa; 4 Go omiša ka 100-150°C go moyafatša meetse ka bonolo le go bopa filimi ya PTFE ye e omilego; 5 Sintering ka 360-390°C (go fihla go 400°C) go qhibidiša dikarolwana tša PTFE go ba filimi ye e tšwelago pele; 6 Multi-potoloho impregnation-omisa-sintering pheta 2-4 makhetlo a ho fihlela sepheo botenya le resin dikahare (45-65%); 7 Kalafo ya ka morago go akaretšwa kalafo ya corona, go kgaola mošito, go sotha le go hlahloba boleng. Dintlha tša taolo ya motheo: dewaxing ka botlalo, go kolobiša ka botlalo ka emulsion, go omišwa ganyenyane-ganyenyane, themperetšha ya sintering ye e nepagetšego, le segokanyipalo sa go tlotša se se sa fetogego. Dihlahiswa sebeletsa phahameng-maqhubu a koporo-apere laminates, phahameng-mocheso conveyor mabanta le mehaho lera thepa.

Sehlogo se se akaretša ditšhupetšo tša motheo tša tshepedišo ya theipi ya themperetšha ya godimo ya PTFE yeo e šomišwago ka go tlotša ka lefeela, kalafo ya phišo ya lefeela le ditikologo tše di swanago. Dinyakwa tše bohlokwa di fapana kudu le tšhomišo ya lefaufau: go ntšha kgase go bohlokwa kudu (TML≤1%, CVCM≤0.1%; mephato ya sefofane/ya optical e nyaka TML≤0.5%, CVCM≤0.01%); go ganetša themperetšha go swanetše go netefatšwa bakeng sa bobedi substrate ya PTFE (260°C) le legato la sekgomaretši; silicone PSA yeo e hlwekišitšwego ka mo go kgethegilego ya go ntšha kgase ya fase e a nyakega go thibela tšhilafalo ya siloxane; phahameng-mocheso tšoara matla thibela creep le bohale phahamisa; bohlweki ga bo nyake go tšhollwa ga tlhale le diteng tša tlase tša ionic; theipi-ba khahlanong le static (bokagodimo resistivity 106-109 Ω / sq) thibela ESD tšenyo; go ganetša ga plasma go swanetše go hlahlobja bakeng sa ditshepedišo tša go sputtering/PECVD; go fokotšega ga phišo ka fase ga 2% go netefatša go nepagala ga masking.

Sehlogo se se tsebiša disolvent tša organic tšeo lešela la themperetšha ya godimo ya PTFE le ka di kgotlelelago. Lešela la fiberglass leo le tloditšwego ka PTFE le bontšha go se šome ga dikhemikhale mo go kgethegilego, le ganetša mo e nyakilego go ba disolvent ka moka tše di tlwaelegilego tša organic ka fase ga maemo a tlwaelegilego a mošomo ntle le go phatlalatšwa, go ruruga goba karabelo ya dikhemikhale. Dihlopha tše di kgotlelelwago di akaretša: di-alcohol (methanol, ethanol, isopropanol), di-ketone (acetone, MEK, cyclohexanone), di-ester (ethyl acetate, butyl acetate), dikhaponetaeoksaete (peterole, toluene, xylene, hexane), dikhaponetaeoksaete tše di nago le halogen (dichloromethane, chloroform, carbon tetrachloride), di-ether (diethyl ether, THF), diesiti tša organic (esiti ya asetiki ya leqhwa, esiti ya formic), di-amine le di-amide (triethylamine, DMF), di-phenol, le tše dingwe tše bjalo ka khapone disulfide, pyridine, oli ya silicone le seela sa diporiki.

Sehlogo se se akaretša dinyakwa tša seelo sa go tonya nakong ya go sintering ga lešela la themperetšha ya godimo ya PTFE. Ka morago ga go sintering ka 380-400°C, lešela le swanetše go feta ka lebelo ka lefelong la 310-315°C leo le nago le kwelobohloko ya kristale. Sekgahla sa go fodiša se se kgothaletšwago ke bonyane 30-50°C/min (lešela le lesesane le ka fihlelela 100-200°C/min ka go fodiša moyeng). Go fodiša ka lebelo (go tima) go tšweletša crystallinity ya fase (45-50%), go tšweletša dilo tše boleta, tše thata tša go tlotša ka bokagodimo bjo bo boreledi, go kgomarela ka maatla, tshepedišo ye botse kudu ya go se kgomarele, le go ganetša delamination le go phatloga. Go fodiša ka go nanya (go tonya ga sebjana) go feletša ka kristale ya godimo (60-70%), go hlola dikhupetšo tše di thata, tše di brittle tšeo di sekametšego go fokotšega, go ebola le go phatloga ga microcracks.

Sehlogo se se bapetša go butšwa ga themperetšha ya phapoši le ya themperetšha ya godimo ya sekgomaretši seo se nago le kgatelelo ya silicone bakeng sa theipi ya PTFE. Go butšwa ga themperetšha ya godimo (120-180°C) go hlola dinetweke tše di kitimago tše di kgokagantšwego ka maatla a go kgokagana a maatla, go thibela mašaledi a sekgomaretši ka morago ga go ebola. E bopa ditlemo tša go tsenya dikhemikhale le disubstrate tša PTFE ka go fodiša mmogo ga primer, go fediša dikotsi tša delamination. Go butšwa ga themperetšha ya godimo gape go tloša dilo tše di sa tsepamago tša dimolekule tša fase pele ga pelego, go thibela go bubble le tšhilafatšo ya oli ya silicone nakong ya go ruthetša la mathomo.