Ekitabo kino kikwata ku PTFE high-temperature tape okulonda for injection molding demolding n'okukozesa anti-stick. Okulonda okusinziira ku bbugumu: ≤260°C ku buveera obw’awamu (standard silicone PSA tape, 0.13-0.18mm); 260-300°C ku buveera bwa yinginiya obw’ebbugumu eringi nga PC, PA66, POM (ekisiiga kya silikoni eky’ebbugumu erya waggulu, 0.18-0.25mm); 300-400°C ku PEEK, LCP, PPS okumpi n’abaddusi ababuguma (tepi eyesiiga eremererwa; kozesa olugoye lwa PTFE olutaliimu kwesiiga oba firimu ya PFA). Okulonda okwesigamiziddwa ku bintu: ebintu ebikwatagana (tacky materials) byetaaga high-release pure PTFE surfaces; ebintu ebijjudde endabirwamu/eby’obuggagga bw’omu ttaka byetaaga obutambi obuzitowa obwa mm 0.25+ obugumira okwambala; ebirungo ebikulukuta byetaaga ebizigo ebigumira eddagala n’ebintu ebinene; enkola ezikwata ku static zeetaaga anti-static black PTFE tape.

Olugoye olw’ebbugumu eringi olwa PTFE olusika ennyo lukolebwa nga lusiiga PTFE ku lugoye lwa fiberglass olw’amaanyi amangi, nga luwa amaanyi g’okusika, okugumira ebbugumu, eby’obugagga ebitakwata, okuziyiza eddagala, n’okusikagana okutono. Ebikulu ebikozesebwa mulimu: okutambuza mu makolero (okupakinga ebbugumu okukendeeza, okufumba emmere, okukala engoye, okukala empapula/firimu); composite molding release olugoye ne hot press cushion liners; okuweta kateni ezikuuma n’obukooti obuziyiza ebbugumu; okuziyiza mmotoka z’amasannyalaze ne tulansifooma; okuzimba bbeeri ezisereka n’ebiwanirira payipu; okusengejja eddagala n’okusiba vvaalu mu mbeera ezivunda. Amaanyi g’okusika amangi gakakasa okuwangaala wansi w’okusika, okukutuka, okunyiga enfunda eziwera, n’okunyigirizibwa kw’ebyuma okw’ebbugumu eringi mu nkola zino ez’enjawulo ez’emirimu emizito.

Mu kiseera ky’okusiba, obutundutundu bwa PTFE ku lugoye lwa fiberglass busaanuuka waggulu wa 327°C, ne busaanyaawo lamelae ez’olujegere oluzingiddwa olw’olubereberye n’ensalosalo z’obutundutundu okukola okusaanuuka okutali kwa kifaananyi. Nga enyogoze, PTFE eddamu okufuuka ekiristaayo ne kifuuka spherulites ezikoleddwa mu lamellae ezitunudde mu radially, nga crystallinity ziri wakati wa 50–70%. Omutindo gw’okunyogoza gwe gusalawo okutuukirizibwa kwa kirisitaalo: okunyogoga mpola kuvaamu obuwundo obusingako, spherulites ennene, obukaluba obusingawo; okuzikiza amangu kiwa spherulites ennungi n’okulongoosa mu kukyukakyuka.